Specification
|
product: |
ceramic glass board heating Resist paste |
|
Part number: |
05H09 |
Application:
The resist paste applies to ceramic glass heating resistor paste.
Operating conditions：
|
Substrate |
Glass ceramic |
|
Printing |
200-250 mesh stainless screen |
|
Levelling |
5-15min minutes at room temperature |
|
Drying |
100-150℃ 10-15 min |
|
Firing Condition |
Atmospheric firing in belt furnace with peak time of 10 Minutes at 800℃ |
|
Thinner |
ST1001 |
Characteristics：
Paste Characteristics：
|
Characteristic |
Standard |
Test method and conditions |
|
|
1 |
Fineness |
≤8μm |
FOG test |
|
2 |
Viscosity |
120-280Pa.s |
Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm, 25±1℃， Brookfield HBT |
Characteristics after firing：
Check fired film produced under the conditions specified in 1）, (Film thickness is 8-12mm.)
|
Characteristics |
Standard
|
Test method and conditions |
|
|
3 |
Appearance |
Compact and unknit |
Eyeballing |
|
4 |
Resistivity |
As below form |
Standard film thickness is 10mm. |
|
TCR |
As below form |
HTCR 25-125℃ |
|
|
Product series |
Ceramic glass board heating Resist paste |
|||
|
P/N |
resistivity (Ω/□) |
TCR (ppm/℃) |
Sintering temperature℃ Sintering |
viscosity (kcps) |
|
05H09-0R01012 |
0.01 |
1200 |
800℃ |
120～280 |
|
05H09-0R02012 |
0.02 |
1200 |
||
|
05H09-0R03012 |
0.03 |
1200 |
||
|
05H09-0R04012 |
0.04 |
1200 |
||
|
05H09-0R05012 |
0.05 |
1200 |
||
|
05H09-0R10012 |
0.10 |
1200 |
||
|
05H09-0R50012 |
0.50 |
1200 |
||
|
05H09-1R00012 |
1.00 |
1200 |
||
|
05H09-5R00012 |
5.00 |
1200 |
||
|
|
|
|
|
|
|
05H09-0R01030 |
0.01 |
3000 |
800℃ |
120～280 |
|
05H09-0R02030 |
0.02 |
3000 |
||
|
05H09-0R03030 |
0.03 |
3000 |
||
|
05H09-0R04030 |
0.04 |
|
||