| P/N |
Composition |
Firing Temperature |
Key Features & Applications |
Datasheet |
| 01L-3611D |
Low-temperature silver paste |
80-200℃ |
Low-temperature baked electrode silver paste |
Click to view details |
| 01L-3608B |
Adhesive conductive adhesive |
150~300℃ |
Used for bonding piezoelectric ceramic sheets and ceramics, metals. The highest temperature resistance is 300℃ for a long time, and 350℃ for a short period (2 hours). |
Click to view details |
| 01M-3605 |
Sintered silver paste |
600℃ |
Medium-temperature sintered polar silver paste, with a relatively wide sintering temperature range of 500 - 750℃. This type is widely used in industrial production and is highly recommended. |
Click to view details |
| 01H-3605 |
Sintered silver paste |
850℃ |
High-temperature sintered polarized silver paste. After sintering, the metal film can conduct electricity at high temperatures, with a maximum temperature resistance of 800℃. |
Click to view details |
| 01M-6301 |
Bonding silver paste |
500~800℃ |
Used for bonding piezoelectric ceramic sheets and ceramics, as well as metals. The maximum temperature resistance is 800℃ for a long period of time. |
Click to view details |
| 02H-3620 |
Silver palladium paste |
850~1050℃ |
Multi-layer piezoelectric ceramic stack-fired inner electrodes, with a wide sintering temperature range of 850~1050℃, with a maximum temperature resistance of 1050℃ |
Click to view details |
| 02H-3630 |
Silver palladium paste |
850~1100℃ |
Multi-layer piezoelectric ceramic laminated internal electrodes, with a wide sintering temperature range of 850~1100℃, with a maximum temperature resistance of 1100℃ |
Click to view details |
| 02H-3640 |
Silver palladium paste |
850~1150℃ |
Multi-layer piezoelectric ceramic stack-fired inner electrodes, with a wide sintering temperature range of 850~1150℃, with a maximum temperature resistance of 1150℃ |
Click to view details |
| 02H-3650 |
Silver palladium paste |
850~1200℃ |
Multi-layer piezoelectric ceramic stack-fired inner electrodes, with a wide sintering temperature range of 850~1200℃, with a maximum temperature resistance of 1200℃ |
Click to view details |
| 55H-1803 |
Platinum paste |
850~1300℃ |
Platinum electrodes, sintered at 850 - 1300℃, meet the requirements of most external electrodes and high-temperature co-sintering, and can be repeatedly sintered multiple times. |
Click to view details |
| 55H-1803D |
Platinum paste |
1000~1300 ℃ |
Commonly used platinum electrodes, sintered at a temperature range of 1000 to 1300℃. The sensor sintered electrode can withstand a temperature of 1400 to 1500℃. It can meet the requirement of long-term operation within 1000℃ and can be re-fired multiple t |
Click to view details |