Specification
|
product: |
Thick Film Resist paste |
|
Part number: |
05H01 series |
Application:
This specification of resistance paste applies to chip Resistor, thick film circuit.
Operating conditions：
|
Substrate |
96% alumina、surface roughness 3-5μm |
|
Printing |
200-250 mesh stainless screen |
|
Levelling |
5-15min minutes at room temperature |
|
Drying |
100-150℃ 10-15 min |
|
Firing Condition |
Atmospheric firing in belt furnace with peak time of 9-11 Minutes at 850±2℃ |
|
Thinner |
ST1000，ST1001 |
Characteristics：
Paste Characteristics：
|
Characteristic |
Standard |
Test method and conditions |
|
|
1 |
Fineness |
≤8μm |
FOG test |
|
2 |
Viscosity |
100-200Pa.s |
Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm, 25±1℃， Brookfield HBT |
Characteristics after firing：
Check fired film produced under the conditions specified in 1）, (Film thickness is 8-12mm.)
|
Characteristics |
Standard
|
Test method and conditions |
|
|
3 |
Appearance |
Compact and unknit |
Eyeballing |
|
4 |
Resistivity |
As below form |
Standard film thickness is 10mm. |
|
TCR |
As below form |
HTCR 25-125℃, CTCR 25~-55℃ |
|
|
ESD |
As below form |
1000V 1s 5times |
|
|
|
STOL |
As below form |
Unit Power 1/8W/mm2 2.5 rating voltage（Max 400V），5seconds |
| Product series | Thick film circuitry uses resistor paste | |||||
|
Product NO
|
（Ω/□） |
Tolerance % |
Main Compositions |
TCR （ppm/℃） |
ESD （%） |
Firing Temp（℃） |
|
05H01-0R1 |
0.1 |
±15% |
Ag、 Pd 、RuO2 |
-200～+700 |
±1 |
Aerodynamic atmosphere sintering at 850℃ Peak value for 10 minutes Please request the sintering curve |
|
05H01-0R2 |
0.2 |
±15% |
Ag、 Pd 、RuO2 |
-200～+700 |
||
|
05H01-1R0 |
1.0 |
±15% |
Ag、 Pd 、RuO2 |
-200～+500 |
||
|
05H01-4R0 |
4.0 |
±15% |
Ag、 Pd 、RuO2 |
-200～+500 |
||
|
05H01-5R0 |
5.0 |
±15% |
Ag、 Pd 、RuO2 |
-200～+300 |
||
|
05H01-6R0 |
6.0 |
±15% |
Ag、 Pd 、RuO2 |
±100 |
||
|
05H01-8R0 |
8.0 |
±15% |
Ag、 Pd 、RuO2 |
|||
|
05H01-011 |
10 |
±15% |
Ag、 Pd 、RuO2 |
|||
|
05H01-021 |
20 |
±15% |
RuO2 |
|||
|
05H01-051 |
50 |
±15% |
RuO2 |
|||
|
05H01-101 |
100 |
±15% |
RuO2 |
|||
|
05H01-102 |
1K |
±15% |
Pb2Ru2O6 |
|||
|
05H01-103 |
10K |
±15% |
Pb2Ru2O6 |
|||
|
05H01-104 |
100K |
±15% |
Pb2Ru2O6 |
|||
|
05H01-105 |
1M |
±15% |
Pb2Ru2O6 |
±200 |
||
|
05H01-106 |
10M |
-30% |
Pb2Ru2O6 |
|||
|
05H01-107 |
100M |
-30% |
Pb2Ru2O6 |
|||
Storage condition and Term of validity
The product should be stored in a sealed manner at an ambient temperature ranging from 5 to 25 degrees Celsius. The validity period is six months from the date of shipment.
Packaging method：
1000g/can