Specification
|
product: |
Silver paste |
|
Part number: |
01M-0605 series |
Application:
This Specification applies to piezoceramic conductive paste.
Operating conditions：
|
Substrate |
3-5u， piezoceramic |
|
Printing |
200-300 mesh stainless screen |
|
Levelling |
5-15min minutes at room temperature |
|
Drying |
100-150℃ 10-15 min |
|
Firing Condition |
Atmospheric firing in belt furnace with peak time of 9-11 Minutes at 550-750℃ |
|
Thinner |
ST-1000 |
Characteristics：
|
|
01M-0605 |
01M-0607 |
|
Fineness(um) |
≤5 |
|
|
Viscosity(pa.s) |
120-280 |
|
|
Solid content（%） |
70-75 |
60-65 |
|
Resistivity(mΩ/□) |
≤3 |
≤5 |
|
Adhesion(N) |
≥45 |
≥42 |
|
Advantages |
Excellent soldering performance |
|
|
Standard |
Test method and conditions |
|
Fineness |
FOG test |
|
Viscosity
|
Brookfield HBT utility cup and spindle (SC4-14/6R), 10rpm, 25±1℃， Brookfield HBT
|
|
Resistivity
|
Fired film thickness is 8-12mm.) Test pattern 0.6mm×60mm |
|
Adhesion strength
|
Peel Test: 0.5mmφ Tin plated Cu wire soldered on 2mm×2mm Pad. Solder: 96.5Sn/0.5Cu Mildly activated flux used. |
Storage condition and Term of validity
The product shall be guaranteed for 1 year after shipping date, keep tightly under at 5-25℃
Packaging method：
Standard package： 1000g/can，
Sample package: 200g/can